Synthesis and characterization of double solid solution (Zr,Ti)(2)(Al,Sn)C MAX phase ceramics
| |
|
Author
|
|
|
|
| |
|
Abstract
|
|
|
|
| Quasi phase-pure (>98 wt %) MAX phase solid solution ceramics with the (ZryTi)(2)(Al-0.5,Sn-0.5)C stoichiometry and variable Zr/Ti ratios were synthesized by both reactive hot pressing and pressureless sintering of ZrH2, TiH2, Al, Sn, and C powder mixtures. The influence of the different processing parameters, such as applied pressure and sintering atmosphere, on phase purity and microstructure of the produced ceramics was investigated. The addition of Sn to the (Zr,Ti)(2)AlC system was the key to achieve phase purity. Its effect on the crystal structure of a 211-type MAX phase was assessed by calculating the distortions of the octahedral M6C and trigonal M(6)A prisms due to steric effects. The M(6)A prismatic distortion values were found to be smaller in Sn-containing double solid solutions than in the (Zr,Ti)(2)AlC MAX phases. The coefficients of thermal expansion along the < a > and < c > directions were measured by means of Rietveld refinement of high-temperature synchrotron X-ray diffraction data of (Zr1-x,Ti-x)(2)(Al-0.5,Sn-0.5)C MAX phase solid solutions with x = 0, 0.3, 0.7, and 1. The thermal expansion coefficient data of the Ti-2(Al-0.5,Sn-0.5)C solid solution were compared with those of the Ti2AlC and Ti2SnC ternary compounds. The thermal expansion anisotropy increased in the (Zr,Ti)(2)(Al-0.5,Sn-0.5)C double solid solution MAX phases as compared to the Zr-2(Al-0.5,Sn-0.5)C and Ti-2(Al-0.5,Sn-0.5)C end-members. |
| |
|
Language
|
|
|
|
English
| |
|
Source (journal)
|
|
|
|
Inorganic chemistry / American Chemical Society. - Easton, Pa
| |
|
Publication
|
|
|
|
Easton, Pa
:
2019
| |
|
ISSN
|
|
|
|
0020-1669
| |
|
DOI
|
|
|
|
10.1021/ACS.INORGCHEM.9B00065
| |
|
Volume/pages
|
|
|
|
58
:10
(2019)
, p. 6669-6683
| |
|
ISI
|
|
|
|
000469304700014
| |
|
Pubmed ID
|
|
|
|
31042023
| |
|
Full text (Publisher's DOI)
|
|
|
|
| |
|
Full text (publisher's version - intranet only)
|
|
|
|
| |
|